OK Autrod 316LSi

The following items have been added to your list


x

A continuous, solid, corrosion-resistant, chromium-nickel-molybdenum wire for welding austenitic stainless alloys of the 18% Cr -8% Ni and 18% Cr -10% Ni -3% Mo types. OK Autrod 316LSi has good general corrosion resistance; in particular, the alloy has very good resistance to corrosion in acid and chlorinated environments. The alloy has a low carbon content which makes it particularly recommended when there is a risk of intergranular corrosion. The higher silicon content improves the welding properties such as wetting. The alloy is widely used in the chemical and food processing industries, as well as in shipbuilding and various types of architectural structure.


Typical Charpy V-Notch Properties

Impact Value Testing Temperature
as welded
70 J (52 ft-lb) -110 degC (-166 degF)
45 J (33 ft-lb) -196 degC (-321 degF)
95 J (70 ft-lb) -60 degC (-76 degF)
120 J (89 ft-lb) 20 degC (68 degF)

Typical Tensile Properties

Condition As Welded As Welded
Shielding Gas Tested at 350°C.
Tensile Strength 560 MPa (81 ksi) 440 MPa (64 ksi)
Yield Strength 400 MPa (58 ksi) 340 MPa (49 ksi)
Elongation 37 % 26 %

Recommended Welding Parameters

Wire Diameter
0.6 mm (0.025 in.)
1.14 mm (0.045 in.)

Deposition Data

Current Deposition Rate Diameter Voltage Wire Feed Speed
65-220 A 1.1-5.4 kg/h (2-11 lb/h) 0.9 mm (0.035 in.) 15-28 V 3.5-18.0 m/min (138-709 in./min)
80-240 A 1.5-6.0 kg/h (3-13 lb/h) 1.0 mm (0.040 in.) 15-28 V 4.0-16.0 m/min (157-630 in./min)
100-300 A 1.6-7.5 kg/h (3-16 lb/h) 1.2 mm (0.047 in.) 15-29 V 3.0-14.0 m/min (118-551 in./min)
230-375 A 5.2-8.6 kg/h (11-19 lb/h) 1.6 mm (1/16 in.) 23-31 V 5.5-9.0 m/min (217-354 in./min)
55-160 A 1.0-4.1 kg/h (2-9 lb/h) 0.8 mm (0.030 in.) 12-24 V 4.0-17.0 m/min (157-669 in./min)

Classifications

Wire Electrode SFA/AWS A5.9 : ER316LSi
Werkstoffnummer : ~1.4430
EN ISO 14343-A : G 19 12 3 L Si

Approvals

Approvals CE EN 13479
CWB ER316LSi
DB 43.039.05
DNV-GL VL 316 L (M13)
NAKS/HAKC 0.8-1.2 mm
VdTÜV 04268
Approvals are based on factory location. Please contact ESAB for more information.

Consumable Characteristics

Alloy Type Austenitic (with approx. 8 % ferrite) 19% Cr - 12% Ni - 3% Mo - Low C - High Si

Typical Weld Metal Analysis %

Typical Wire Composition %
C Cr Cu Mn Mo Ni P S Si Si+Fe
0.01 % 18.4 % 0.12 % 1.8 % 2.60 % 12.2 % - - 0.9 % 7 %
Typical Weld Metal Analysis %
0.02 % 18.5 % 0.1 % 1.8 % 2.7 % 12 % 0.015 % 0.015 % 0.8 % -
x

Čia sužinosite, kaip rasti OK Autrod 316LSi

Mes nakantriai laukiame, kol jūs išbandysite mūsų gaminius ir tikime, kad liksite jais patenkinti. Mes orientuojamės į aukščiausią tiek produktų, tiek ir aptarnavimo kokybę, todėl ESAB gaminius parduodame per aukštus aptaranvimo standartus atitinkančius platintojus, kurie gali jums skirti ir dėmesį, ir suteikti pagalbą bei pasiūlyti priimtiniausią sprendimą.

Kad viskas būtų dar paprasčiau, žemiau pateikiame internetinį pirkinių sąrašą. Naršydami mūsų tinklapyje ir spustelėję bet kurį norimą gaminį, galėsite jį nesunkiai įkelti į šį puslapį. Baigę sąrašą galėsite atsisiųsti sau arba atsispausdinti ir nusinešti pas pasirinktą platintoją.

Norėdami rasti ESAB platintoją, pasinaudokite kiekviename mūsų žiniatinklio puslapyje esančia RASKITE PLATINTOJĄ funkcija. Taip pat galite paskambinti mūsų pagalbos linija telefonu ir mes nukreipsime jus teisinga kryptimi.


Užsakymo kodai ir priedai

Part Numbers : OK Autrod 316LSi
1632064600
1632089500
1632089820
1632082110
1632084600
1632099820
1632094600
1632109500
1632109820
1632109890
163210247V
163210932U
1632109320
1632104600
1632119820
1632119320
1632129500
1632129820
163212932U
1632129320
1632129370
163212342W
1632129A00
1632169820
163216342W
1632169410
x
x

x

Loading..