FILARC 76S

FILARC 76S

FILARC 76S is a CTOD-tested, all-positional, basic AC/DC electrode with 100% recovery for offshore fabrication (diameter 4.0 and 5.0 mm 115%). Alloyed with max 1%Ni. Good CVN toughness down to -60°C. CTOD tested in the AW and SR conditions. BS4360-50D steel and similar grades. Satisfactory CTOD results eliminate stress relieving for joints up to approx. 50 mm plate thickness. Many approved welding procedures available. Use short arc. Weave slowly when permitted. DC+. Use DC- for root passes.

Pridėti į krepšelį


Specifikacijos


Typical Tensile Properties

As welded
Apsauginės dujos Elongation Tensile Strength Yield Strength
ISO 28 % 630 MPa 550 MPa
AWS - - -

Čarpio V formos įrantos testo savybės

As welded
Apsauginės dujos Impact Value Testing Temperature
ISO 110 J -40 °C
ISO 75 J -60 °C

Nusėdimo duomenys

Amperai Fusion time per electrode at 90% I max kg weld metal/kg electrodes Number of electrodes/kg weld metal Nusėdimo greitis Skersmuo Voltai
55-85 A 59 sec 0.65 kg 87 0.7 kg/h 2.5 x 350 mm 24 V
100-125 A 63 sec 0.63 kg 55 1.05 kg/h 3.0 x 350 mm 21 V
80-140 A 60 sec 0.57 kg 54 1.12 kg/h 3.2 x 350 mm 23.8 V
125-175 A 63 sec 0.61 kg 41 1.4 kg/h 3.5 x 350 mm 21.6 V
120-180 A 78 sec 0.63 kg 31 1.51 kg/h 4.0 x 350 mm 22 V
120-170 A 109 sec 0.608 kg 24 1.4 kg/h 4.0 x 450 mm 22.2 V
180-270 A 106 sec 0.62 kg 15 2.22 kg/h 5.0 x 450 mm 24.3 V

Suvirinimo metalo analizė

Mn
MnMoCSiNiCr
1.58 % - - - - -
Mo
MnMoCSiNiCr
- 0.01 % - - - -
C
MnMoCSiNiCr
- - 0.05 % - - -
Si
MnMoCSiNiCr
- - - 0.36 % - -
Ni
MnMoCSiNiCr
- - - - 0.87 % -
Cr
MnMoCSiNiCr
- - - - - 0.04 %

Patvirtinimai: ABS, 3Y H5, BV, 3Y H5, CE, EN 13479, DNV-GL, 3 YH5, LR, 5Y42 H5, Seproz, UNA 272581
Klasifikacijos: SFA/AWS A5.5, E7018-G, EN ISO 2560-A, E 46 6 Mn1Ni B 32 H5

Approvals are based on factory location. Please contact ESAB for more information.


Alloy Type: Low alloyed (0.9 % Ni)
Coating Type: IMPERIAL_Basic covering
Diffusible Hydrogen: < 5.0 ml/100g
Welding Current: AC, DC+-